Associated changes in stiffness of collagen scaffolds during osteoblast mineralisation and bone formation

Abstract

Objective

Engineering bone in 3D is important for both regenerative medicine purposes and for the development of accurate in vitro models of bone tissue. The changing material stiffness of bone tissue had not yet been monitored throughout the process of mineralisation and bone nodule formation by osteoblasts either during in vitro engineering or in development perspective.

Results

Within this short research note, stiffness changes (Young’s modulus) during in vitro bone formation by primary osteoblasts in dense collagen scaffolds were monitored using atomic force microscopy. Data analysis revealed significant stiffening of 3D bone cultures at day 5 and 8 that was correlated with the onset of mineral deposition (p < 0.00005).

Introduction

Bone tissue forms when differentiated bone cells, osteoblasts, deposit the appropriate matrix proteins, composed of an inorganic and organic matrix component. Through development or maturation of bone, the matrix component changes in structure and composition, thus altering the material properties of bone [1]. Osteoblasts synthesise bone matrix in two steps: (1) secreting collagen proteins (collagen type I) and non-collagen proteins including osteocalcin, osteonectin and bone sialoprotein II; (2) mineralisation and formation of the hydroxyapatite crystals. Hydroxyapatite crystals are formed through the deposition of mature apatite minerals. Furthermore collagen I is remodelled through increases in fibril diameter, orientation and cross-linking [2, 3].

Biophysical parameters, including stiffness, are essential to define the mechanical integrity of bone. The mechanical properties of fully formed bone are well defined [4, 5]. Even so, the changing material properties of developing bone are not well understood and have not been extensively studied. There is a significant relationship between tissue stiffness and mineralisation but no significant difference in tensile strength between foetal bone and bone from new-born animals [6].

The process of mineralisation and bone nodule formation by osteoblasts is of particular interest. Monitoring the resultant changes in stiffness of a collagen scaffold caused by the cellular processes of mineralisation through to bone formation is challenging, but of immense interest as we decipher the changing material properties of developing bone. Bone forming-cells, osteoblasts have been widely used for in vitro bone formation studies. It is possible to culture neonatal rodent calvarial osteoblasts which form mature bone nodule formation in vitro in 2D [7, 8]. This process is enhanced when culturing primary osteoblasts in dense collagen (10%) scaffolds [9]. Bakkalci et al. have shown that by culturing primary osteoblast cells in 3D dense collagen, there is a significant increase in mineralisation and formation of large bone nodules compared to 2D [9]. This short note focuses on mineralisation and bone nodule formation and the effect these processes have on the changing stiffness of a 3D collagen scaffold.

Stiffness measures the deformation of a material under certain applied force [10, 11]. Its usual measure is the elastic modulus, also called Young’s Modulus (E). The stiffness unit is determined from stress over strain, Pa or N/m2 [11]. In tissues, the stiffness is based on the composition of the extracellular matrix. The tissue stiffness of bone is significantly higher (at 15 MPa) compared to other tissues such as brain (1 kPa) and articular cartilage (6 kPa) [12]. Techniques to complete ex vivo measurements for mechanical characterisation include atomic force microscopy (AFM), microindentation, and shear rheometry [13,14,15,16]. AFM can be used for both single cell level and bulk tissue level mechanical measurements.

Mineralisation and maturation of the inorganic component of bone determines the high strength and stiffness of bone tissue, with collagen playing a minor component [17]. Herein, we utilised AFM to measure changes in the stiffness of an osteoblast seeded dense collagen scaffold during the processes of mineralisation through to bone nodule formation. We correlated the stage-specific genes associated with bone formation, to changes in stiffness measurements.

Main text

Materials and methods

Isolation of primary rat osteoblasts

The primary calvarial rat osteoblasts were isolated, passaged and characterised as described in [9, 18, 19]. The cells were cultured for 3 days until they have reached confluency prior to 3D set-up at 37 oC, 5% CO2 in α-MEM (Gibco through Thermo Fisher Scientific, Loughborough, UK), supplemented with 10% Foetal Bovine Serum, 2 mM L-glutamine (Life Technologies). Different techniques were used to characterise osteoblasts and osteoblast-driven bone formation and these include analysis of osteoblast gene markers and Alizarin red staining as described in [9].

Fabrication of 3D bone model

The osteoblasts were seeded in 2D (control) or 3D soft collagen scaffolds (0.2% collagen), or dense collagen scaffolds (10% collagen) in 24-well plates [20]. 3D soft and dense collagen scaffolds were prepared as described in [9] (pages 3–10). A mix of 10X Minimal Essential Medium (MEM) (Sigma-Aldrich, Dorset, UK), monomeric type I collagen, (First Link, Birmingham, UK) and the neutralising agent composed of 17% of 10 Molar (M) NaOH (Sigma-Aldrich, Dorset, UK) and 83% 10 M HEPES buffer (Gibco through Thermo Fisher Scientific, Loughborough) was prepared. Finally, a cell suspension of 7 × 104 cells/well was added to this mix. 1.3 ml of cell/mix with 7 × 104 cells per well were polymerised for 15 min at 37 oC. For dense collagens plastic compressed using 24-well RAFT absorbers (Lonza, Slough, UK), where for soft collagens the gels were left uncompressed.

Bone formation with bone morphogenic agents

Culture media was replaced with α-MEM supplemented with the bone morphogenic agents (BMA). BMA was composed of 2 mM β-glycerophosphate, 10 nM dexamethasone, and 50 µg/ml ascorbate (Sigma-Aldrich, Dorset, UK).

Characterisation of bone nodules

Brightfield images were taken using the Zeiss AxioObserver with Apotome0.2 instrument and software (Zeiss, Oberkochen, Germany). Observation of the black dots represented mineralisation based on the classification of Orriss et al. [7]. The nodules with sharp, defined margins were identified as bone nodules.

Alizarin Red Staining

Calcium deposition was detected using Alizarin red staining (Sigma-Aldrich, Dorset, UK) at days 5, 8 and 14. The samples were formalin fixed (Genta Medical, York, UK), then washed with ddH2O and incubated with Alizarin red stain for 30 min followed by washing with ddH2O.

Haematoxylin and eosin staining

Formalin-fixed 3D samples were processed and wax embedded (Leica Biosystems, Germany). Samples were sectioned (5 μm) using a microtome (Leica, Milton Keynes, UK) and oven baked at 64 oC. The haematoxylin and eosin (H&E) staining was completed as described in [9].

RNA extraction, cDNA synthesis, qPCR

RNA extraction, cDNA synthesis and qPCR were completed as described in [9]. For each condition, a minimum of 3 replicates were made. The RNA was extracted using TRI Reagent and was subjected to the chloroform induced phase separation method [21], with quality and quantity determined using a Nano-Drop (Thermo Fisher Scientific, Loughborough, UK). The RNA was transcribed into cDNA using High-Capacity cDNA Reverse Transcription Kit (Applied Biosystems through Fisher Scientific, Loughborough, UK). The primer design for the mineralisation gene alkaline phosphatase ALPL and the osteocyte gene E11 designed by Bakkalci et al., [9] were used. The target genes were amplified using iTaq Universal SYBR Green Supermix. For each 10 µl qPCR reaction, 20 ng sample and 0.2 µM primer concentration were used. The CFX96 Touch System (Bio-Rad, Watford, UK) was used to run 40 cycles for the reaction. The ∆CT and 2−∆∆CT methods [22] were followed to assess the relative gene expression normalised to the reference gene Glyceraldehyde 3-phosphate dehydrogenase (GAPDH) [23].

Atomic Force Microscopy (AFM) for stiffness measurements

The 3D samples were tested with an AFM (CellHesion® 200, JPK, Germany) on day 1, 5, and 8 following previously published methodology [24]. Briefly, for each time point, three 3D bone models and three 3D acellular controls were measured. Measurements were performed at room temperature, in Leibovitz’s L-15 Medium, no phenol red (Gibco™ through Fisher Scientific, Loughborough, UK). A stiff cantilever of spring constant of approximately 2 N/m (RFESP-75, Bruker) with a glued glass bead of 50 μm in diameter (Cospheric, California, USA) was used to probe the samples. Each sample was probed along a 4 × 4 map of 1500 × 1500 μm leading to a total of 16 measurements per sample. The set force was 700 nN to ensure an indentation of 10 μm minimum (< 10% of total height of the model). The Hertz model was fitted to the collected force curves to determine the Young’s Modulus E, assuming a Poisson ratio of 0.5 [25]. Data for each time point was normalised to its corresponding 3D acellular control of either soft or dense collagen scaffolds, as to obtain percentage change (% change = (E-Econtrol)/Econtrol).

Height measurement

Day 21 bone nodules formed in 3D dense collagen were air-dried in a Petri dish for 24 h. Air-dried collagen layer was defined as the baseline during height measurement and the height relative to the collagen layer was taken measured by Keyence VHX-7000 Digital Microscope (Keyence, Osaka, Japan).

Statistical analysis

All statistical analyses were conducted by using GraphPad Prism 9 Software Inc., La Jolla, CA, US for each condition with minimum of 3 experimental repeats. Shapiro-Wilk test (n\(\ge\)3) or D’Agostino test (n\(\ge\)8) was used as normality test for all data sets. The appropriate statistical significance tests were selected depending on the result of the normality test. The data in the graphs were provided as mean \(\pm\) standard error mean (SEM), and in the text as mean \(\pm\) standard deviation (SD). P-value < 0.05 was taken as statistical significance.

Results

Bone nodules do not form in soft collagen scaffolds

To support our previous finding on bone nodule formation in 3D dense collagen scaffolds, we seeded primary calvarial rat osteoblasts in 3D soft collagen scaffolds and in 3D dense collagen scaffolds for 21 days and bone nodule formation was compared with 2D control cultures (Fig. 1A). Osteoblasts did not deposit bone nodules in the soft collagen scaffolds, where the average stiffness was 39.06 ± 6.73 Pa (Fig. 1B). Mineralisation and hydroxyapatite crystals were significantly reduced in these soft collagen scaffolds compared to 2D and 3D dense collagen scaffolds (Fig. 1A and C). The average number of bone nodules in 3D dense collagen scaffolds was higher compared to 2D culture (Fig. 1A and C). The timeline of the bone nodule formation in 3D dense collagen scaffolds is described in Fig. 1D. The matrix maturation and mineralisation were visible by day 5, where the nodule formation began by day 8. Height measurement images show defined edges of the bone nodules and the nodule protrusion from the 3D dense collagen (Fig. 1D).

Fig. 1
figure 1

The schematic has been created using SmartServier Medical Art

In vitro bone nodule formation. Bone formation in a 2D, b 3D soft collagen scaffold, and c 3D dense collagen scaffold at 14 of BMA application. 2.5× Magnification, Scale bar = 500 μm. d Bone nodule formation timeline in 3D dense collagen. Height measurement of 21-day old bone nodules by Keyence VHX-7000 Digital Microscope (Keyence, Osaka, Japan). Scale bar (left image) = 10 μm.

Mineralisation increases the overall matrix stiffness of engineered bone in 3D dense collagen scaffolds

Previous work has demonstrated that culturing primary osteoblasts in 3D dense collagen results in earlier and more extensive mineralisation and bone nodule formation [9]. The impact of mineralisation and bone nodule formation on the increasing stiffness of collagen scaffolds was measured using AFM. Mineralisation starts on day 5 in dense 3D scaffolds (Fig. 2A), confirmed by using alizarin red staining (Fig. 2D). By day 8, it was possible to visualise dense mineral deposits, osteoblast clusters and small bone nodules (Fig. 2B and C). The cuboidal mononuclear appearance of osteoblasts and mineral deposits was detected by day 8 (Fig. 2C). The sharp edges of the bone nodules were indicative of bone nodule formation and were verified by alizarin red staining (Fig. 2E). The alizarin red staining confirmed the formation of large bone nodules (Fig. 2F).

Fig. 2
figure 2

In vitro bone nodule formation in 3D dense collagen scaffolds. a Mineral deposition at day 5, Scale bar = 500 μm. b Osteoblast clusters and mineral and bone nodule deposition at day 8, Scale bar = 500 μm. c Bone nodule formation at day 8, Scale bar = 100 μm. Alizarin red stained 3D dense collagen scaffolds at d day 5 and e day 8. f Alizarin red stained 3D dense collagen scaffolds at day 8, Scale bar = 25 μm. g Percentage change in stiffness (%) at day 1, 5, and 8. Expression of h ALPL, and i E11 at days 1, 5, and 8. One-Way ANOVA, Dunnet’s Post Hoc; p-values 0.05< *, 0.005<**, 0.005<*** and 0.00005<****

The average stiffness of an acellular 3D dense collagen scaffold was 3962 ± 685.0 Pa. With the onset of mineral deposition, the stiffness increased by 30% on day 5 (p < 0.00005) and by 35% on day 8 (p < 0.00005) compared to day 1 (Fig. 2G). The average stiffness of the 3D bone model at day 5 was 5473 ± 2725 Pa and at day 8 was 5700 ± 1087 Pa taken as an average over a defined 1500 × 1500 μm area.

The osteoblast and mineralisation marker ALPL [26] was upregulated 39-fold from day 1 to day 8 (p < 0.05) (Fig. 2H). The osteocyte marker E11 [27] increased 2.7-fold at day 5 (p < 0.05) and 4.8-fold at day 8 (p < 0.05) (Fig. 2I).

Discussion

The culture of primary osteoblasts in 3D dense collagen scaffolds results in significant mineralisation and bone nodule formation compared to cultures in 2D and soft collagen scaffolds. It is not surprising that the more biomimetic the collagen type I environment (dense) enhances the osteoblast-driven bone formation considering that collagen I is the main organic ECM protein found in bone [28, 29].

Herein are three novel findings on understanding how stiffness changes during bone formation. The first is that stiffness of the dense collagen scaffold itself is not impacted by the addition of bone morphogenic reagents. The stiffness of the dense collagen was ~ 4 kPa on day 1, compared to soft collagen scaffolds of ~ 40 Pa, indicating that the higher range of stiffness required to initiate bone matrix deposition. The stiffness changes as the tissue develops and therefore the active process of mineralisation on day 5 concords with a significantly increased stiffness observed on the same day (30% increase). The bone nodules were formed on day 8, when stiffness increased by 5% compared to day 5, suggesting a stiffness threshold that should be achieved in vitro to initiate mineralisation and bone formation. After reaching the stiffness threshold, the increase in stiffness is more limited. The small increase in stiffness percentage change and large standard deviation can be explained by the averaging method used. AFM measures were taken every 375 μm (1500 × 1500 μm area), and then averaged, thus minimising biased results, and avoiding solely focusing on mineral points and bone nodules. Instead, both acellular and mineralised areas of a sample are measured at random, leading to the average stiffness increasing with the frequency of minerals and nodules per sample.

This work is the first to quantify in vitro bone nodule formation and ossification by osteoblasts with increasing tissue stiffness. We have optimised an active bone forming model in 3D dense collagen and characterised how stiffness changes prior to and during the formation of bone nodules. This model closely represents the native starting reference for bone formation, and it allows a platform to study pathological alterations related to bone diseases.

Limitations

  • Bone nodules form randomly throughout the culture and due to consistent AFM measurements for every sample, it may be possible to miss the nodules and mineralisation.

Availability of data and materials

The authors confirm that data and material in this study are presented in main manuscript.

Abbreviations

AFM:

Atomic force microscopy

BMA:

Bone morphogenic agents

H&E:

Haematoxylin & Eosin

GAPDH :

Glyceraldehyde 3-phosphate dehydrogenase

MEM:

Minimal essential medium

qPCR:

quantitative polymerase chain reaction

References

  1. Florencio-Silva R, Sasso GRdaS, Sasso-Cerri E, Simões MJ, Cerri PS. Biology of bone tissue: structure, function, and factors that influence bone cells. Biomed Res Int. 2015;2015:421746.

    Article  Google Scholar 

  2. Blair HC, Larrouture QC, Li Y, Lin H, Beer-Stoltz D, Liu L, et al. Osteoblast differentiation and bone matrix formation in vivo and in vitro. Tissue Eng Part B Rev. 2017;23(3):268–80.

    Article  CAS  Google Scholar 

  3. Boonrungsiman S, Gentleman E, Carzaniga R, Evans ND, McComb DW, Porter AE, et al. The role of intracellular calcium phosphate in osteoblast-mediated bone apatite formation. Proc Natl Acad Sci U S A. 2012;109(35):14170–5.

    Article  CAS  Google Scholar 

  4. Morgan EF, Unnikrisnan GU, Hussein AI. Bone mechanical properties in healthy and diseased states. Annu Rev Biomed Eng. 2018;20:119–43.

    Article  CAS  Google Scholar 

  5. Ehrlich PJ, Lanyon LE. Mechanical strain and bone cell function: a review. Osteoporos Int. 2002;13(9):688–700.

    Article  CAS  Google Scholar 

  6. Mulder L, Koolstra JH, den Toonder JMJ, van Eijden TMGJ. Relationship between tissue stiffness and degree of mineralization of developing trabecular bone. J Biomed Mater Res A. 2008;84(2):508–15.

    Article  Google Scholar 

  7. Orriss IR, Hajjawi MOR, Huesa C, MacRae VE, Arnett TR. Optimisation of the differing conditions required for bone formation in vitro by primary osteoblasts from mice and rats. Int J Mol Med. 2014;34(5):1201–8.

    Article  CAS  Google Scholar 

  8. Herberg S, Varghai D, Alt DS, Dang PN, Park H, Cheng Y, et al. Scaffold-free human mesenchymal stem cell construct geometry regulates long bone regeneration. Commun Biol. 2021;4(1):89.

    Article  CAS  Google Scholar 

  9. Bakkalci D, Jay A, Rezaei A, Howard CA, Haugen HJ, Pape J, et al. Bioengineering the ameloblastoma tumour to study its effect on bone nodule formation. Sci Rep. 2021;11(1):24088.

    Article  CAS  Google Scholar 

  10. Baumgart E. Stiffness–an unknown world of mechanical science? Injury. 2000;31(Suppl 2):14.

    Google Scholar 

  11. Guimarães CF, Gasperini L, Marques AP, Reis RL. The stiffness of living tissues and its implications for tissue engineering. Nat Rev Mater. 2020;5(5):351–70.

    Article  Google Scholar 

  12. Leipzig ND, Shoichet MS. The effect of substrate stiffness on adult neural stem cell behavior. Biomaterials. 2009;30(36):6867–78.

    Article  CAS  Google Scholar 

  13. Krieg M, Fläschner G, Alsteens D, Gaub BM, Roos WH, Wuite GJL, et al. Atomic force microscopy-based mechanobiology. Nat Rev Phys. 2019;1(1):41–57.

    Article  Google Scholar 

  14. Arnold M, Zhao S, Ma S, Giuliani F, Hansen U, Cobb JP, et al. Microindentation - a tool for measuring cortical bone stiffness? A systematic review. Bone Joint Res. 2017;6(9):542–9.

    Article  CAS  Google Scholar 

  15. Micalet A, Moeendarbary E, Cheema U. 3D in vitro models for investigating the role of stiffness in cancer invasion. ACS Biomater Sci Eng. 2021. https://0-doi-org.brum.beds.ac.uk/10.1021/acsbiomaterials.0c01530.

    Article  PubMed  Google Scholar 

  16. Whelan IT, Moeendarbary E, Hoey DA, Kelly DJ. Biofabrication of vasculature in microphysiological models of bone. Biofabrication. 2021;13(3):32004.

    Article  CAS  Google Scholar 

  17. Wang X, Shen X, Li X, Agrawal CM. Age-related changes in the collagen network and toughness of bone. Bone. 2002;31(1):1–7.

    Article  Google Scholar 

  18. Orriss IR, Taylor SEB, Arnett TR. Rat osteoblast cultures. Methods Mol Biol. 2012;816:31–41.

    Article  CAS  Google Scholar 

  19. Orriss IR, Utting JC, Brandao-Burch A, Colston K, Grubb BR, Burnstock G, et al. Extracellular nucleotides block bone mineralization in vitro: evidence for dual inhibitory mechanisms involving both P2Y2 receptors and pyrophosphate. Endocrinology. 2007;148(9):4208–16.

    Article  CAS  Google Scholar 

  20. Al Hosni R, Shah M, Cheema U, Roberts HC, Luyten FP, Roberts SJ. Mapping human serum-induced gene networks as a basis for the creation of biomimetic periosteum for bone repair. Cytotherapy. 2020;22(8):424–35.

    Article  CAS  Google Scholar 

  21. Rio DC, Ares MJ, Hannon GJ, Nilsen TW. Purification of RNA using TRIzol (TRI reagent). Cold Spring Harb Protoc. 2010. https://0-doi-org.brum.beds.ac.uk/10.1101/pdb.prot5439.

    Article  PubMed  Google Scholar 

  22. Rao X, Huang X, Zhou Z, Lin X. An improvement of the 2ˆ(-delta delta CT) method for quantitative real-time polymerase chain reaction data analysis. Biostat Bioinforma Biomath. 2013;3(3):71–85.

    PubMed  PubMed Central  Google Scholar 

  23. Abuna RPF, Oliveira FS, Ramos JIR, Lopes HB, Freitas GP, Souza ATP, et al. Selection of reference genes for quantitative real-time polymerase chain reaction studies in rat osteoblasts. J Cell Physiol. 2018;234(1):749–56.

    Article  Google Scholar 

  24. Kayal C, Moeendarbary E, Shipley RJ, Phillips JB. Mechanical response of neural cells to physiologically relevant stiffness gradients. Adv Healthc Mater. 2020;9(8):e1901036.

    Article  Google Scholar 

  25. Javanmardi Y, Colin-York H, Szita N, Fritzsche M, Moeendarbary E. Quantifying cell-generated forces: Poisson’s ratio matters. Commun Phys. 2021;4(1):237.

    Article  Google Scholar 

  26. Staines KA, MacRae VE, Farquharson C. The importance of the SIBLING family of proteins on skeletal mineralisation and bone remodelling. J Endocrinol. 2012;214(3):241–55.

    Article  CAS  Google Scholar 

  27. Zhang K, Barragan-Adjemian C, Ye L, Kotha S, Dallas M, Lu Y, et al. E11/gp38 selective expression in osteocytes: regulation by mechanical strain and role in dendrite elongation. Mol Cell Biol. 2006;26(12):4539–52.

    Article  CAS  Google Scholar 

  28. Eriksen EF. Cellular mechanisms of bone remodeling. Rev Endocr Metab Disord. 2010;11(4):219–27.

    Article  Google Scholar 

  29. Hassani A, Avci ÇB, Kerdar SN, Amini H, Amini M, Ahmadi M, et al. Interaction of alginate with nano-hydroxyapatite-collagen using strontium provides suitable osteogenic platform. J Nanobiotechnol. 2022;20(1):310.

    Article  CAS  Google Scholar 

Download references

Acknowledgements

We are thankful to T.R.A. for alizarin red staining image that was completed in his lab.

Funding

D.B. receives funding from BISS Charitable Foundation. A.M. is funded by the EPSRC. E.M. is grateful for financial supports from Leverhulme Trust (Project Grant RPG-2018-443), Biotechnology and Biological Sciences Research Council (BB/V001418/1) and Engineering and Physical Research Council (EP/W009889/1).

Author information

Authors and Affiliations

Authors

Contributions

DB designed and completed all the experiments except AFM experiment and analysed all data and wrote the manuscript. AM was involved in experimental planning and performed AFM experiments and analysed AFM data and wrote the manuscript. UC designed and supervised the project and wrote the manuscript. EM supervised the project and the manuscript. RAH was involved in experimental planning.  All authors read and approved the final manuscript.

Corresponding author

Correspondence to Umber Cheema.

Ethics declarations

Ethics approval and consent to participate

All methods were carried out in accordance with relevant guidelines and regulations. All experimental protocols were approved by the University College London Biological Services Ethical Review Committee and licensed under the UK Home Office regulations and the Guidance for the Operation of Animals (Scientific Procedures) Act 1986 (Home Office, London, United Kingdom). The study was carried out in compliance with the ARRIVE guidelines (http://www.nc3rs.org.uk/page.asp?id=1357). Consent to Participate is Not Applicable.

Consent for publication

Not Applicable.

Competing interests

The authors declare no conflict of interests.

Additional information

Publisher’s Note

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Rights and permissions

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/. The Creative Commons Public Domain Dedication waiver (http://creativecommons.org/publicdomain/zero/1.0/) applies to the data made available in this article, unless otherwise stated in a credit line to the data.

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Bakkalci, D., Micalet, A., Al Hosni, R. et al. Associated changes in stiffness of collagen scaffolds during osteoblast mineralisation and bone formation. BMC Res Notes 15, 310 (2022). https://0-doi-org.brum.beds.ac.uk/10.1186/s13104-022-06203-z

Download citation

  • Received:

  • Accepted:

  • Published:

  • DOI: https://0-doi-org.brum.beds.ac.uk/10.1186/s13104-022-06203-z

Keywords